Fireproof Silicone Rubber Coated Fabric of Glass Fiber

May 10, 2017

Silicone Coated Fabrics provides better friction than PTFE Coated Fabrics with very good release properties — especially when Silicone Rubber Coated Fabric is in contact with adhesives and other tacky substances. With continuous use,Silicone Glass Coated Fabric temperatures up to 450°F.

Silicone Coated Fabrics

Fiber Characteristics: C-Glass
Fiber Appearance: Continous Fiber
Size: 3.2mm*1m*25m/Roll
Specification: 1.1mm*1m*50m/roll

Shape: Fiberglass Cloth
Diameter of Filaments: Intermediate Fibers
Glass Composition: C-Glass

Solicone coated Fiberglass Fabric
Silicone rubber coated fiberglass fabric is a fiberglass cloth, which possesses the properties of temperature resistance, anti-corrosion, high strength and is coated with organic silicone rubber.
It is a newly-made product with high properties and multiple applications. Due to its unique and excellent
resistance to high-temperatures, permeability and aging, in addition to its durability, this fiberglass fabric is
widely used in aerospace, chemical industry, large-scale generate electricity equipment, machinery,
metallurgy, nonmetal expansion joint .

Type	Thickness (mm)	Breaking Strength (N/50mm)		burst strength Mpa	peeling strength N/m	Flame retardancy	Weight g/m2
Type	Thickness (mm)	warp	weft	burst strength Mpa	peeling strength N/m	Flame retardancy	Weight g/m2
SRC-0.3	0.30+0.03	≥1800	≥1400	≥1.2	≥450	FV-0	470+50
SRC-0.5	0.50+0.05	≥2000	≥1600	≥2.0	≥450	FV-0	640+60
SRC-1.1	1.10+0.10	≥3800	≥3400	≥2.6	≥450	/	1700+170
SRC-1.5	1.50+0.10	≥3200	≥2800	≥3.0	≥450	/	2300+230

The above is the Fireproof Silicone Rubber Coated Fabric of Glass Fiber we have listed for you. You can submit the following form to obtain more industry information we provide for you.

You can visit our website or contact us, and we will provide the latest consultation and solutions

Share to:

Send Inquiry

Previou:Single Side Coated Silicone Rubber Coated Glass Fiber Fabric

Next:Chemical Resistance Silicone Rubber Coated Fiber Fabric